SAE 1045/AISI 1045 Carbon Steel is a medium carbon steel which is characterized by good weldability, good machinability, high strength and impact properties in either the normalized or hot forged condition.
Description
| Material: | 2mm 5mm 6mm 10mm 20mm astm a36 mild carbon steel plate |
| Thickness: | 0.2-500mm,etc |
| Width : | 1000-4000mm,etc |
| Length: | 2000mm, 2438mm, 3000mm, 3500,6000mm,12000mm,or rolled,etc etc |
| Standard: | ASTM,AISI,JIS,GB, DIN,EN |
| Surface: | Black painted,PE coated,Galvanized,color coated, |
| anti rust varnished,anti rust oiled,checkered,etc | |
| Technique: | Cold Rolled, Hot Rolled |
| Certification: | ISO, SGS,BV |
| price terms: | FOB,CRF,CIF,EXW all acceptable |
| Delivery Detail: | inventory About 5-7; custom-made 25-30 |
| Loading port: | any port in China |
| Packing: | standard export packing (inside:water proof paper,outside:steel covered with strips and pallets) |
| Payment Terms: | T/T, L/C at sight,West Union,D/P,D/A,Paypal |
| Container size: | 20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High) |
| 40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High) | |
| 40ft HC:12032mm(Length)x2352mm(Width)x2698mm(High) |
Equivalent Grade
| GB | DIN | NF | SS | JIS | BS | AISI | ISO |
| 45# | 1.0503 | C45 | 1650 | S45C | IC45/080A47 | 1045 | C45E4 |
Chemical Analysis
| NO. | C | Mn | Si | Cr | Cu | Ni | P | S | ||||||||
| Aisi 1045 | 0.43~0.50 | 0.6~0.9 | 0.10~0.60 | ≤0.40 | ≤ 0.50 | |||||||||||
| DIN1.0503 | 0.42~0.48 | 0.6~0.9 | 0.15~0.35 | ≤0.15 | ≤0.3 | ≤0.2 | ||||||||||
| JIS S45C | 0.42~0.50 | 0.5~0.8 | ≤0.40 | ≤0.40 | ≤ 0.4 | |||||||||||
| GB45 | 0.42~0.50 | 0.5~0.8 | 0.17~0.37 | ≤0.25 | ≤0.25 | ≤0.3 | ≤0.035 | ≤0.035 | ||||||||
Mechanical properties
| Annealing | Forging | Tempering and Hardening | Normalization | |||||||||||||
| Subcritical annealing: 650~700 Isothermal annealing: 820~860 | 1100~850 | Tempering: 550~660 Hardening : 820~860 water | 840~880 | |||||||||||||
Heat Treatment
Soft annealing: heat to 550-650°C, cool slowly.
Hardness after annealing: Max. 269HB
Hardening: 820 - 870 °C
Normalizing temperature: 840-870°C